• Leaded brass is an alpha-beta brass with an addition of lead. It has excellent machinability.

 

Lead increases the machinability of brass as well as increasing its strength and resistance to corrosion. The addition of lead also seals shrinkage pores to provide pressure tightness. Brasses can contain up to 3.5 percent in lead contents, and are classified as low, medium, or high-leaded. Leaded brass may be used to make screws, valves, fittings, bearings, specialty fasteners, architectural hardware, and general purpose machine parts.

 

We are one of the trusted manufacturers, suppliers and exporters of a wide array of Leaded Brass in the industry. These are well known for their unmatched quality, high performance, durability standards, robustness and fine finishing. Our Leaded Brass are fabricated using finest quality raw materials which is further processed using advanced equipment, machinery and assistance of our deft engineers. We present these in different technical specifications and at minimal costs.

Specifications:

• IS4413
• CuZn37
• DTD-627
• 60:40 Brass

 

 

 

Chemical Composition Of Leaded Brass :
Material	Normal Composition	Nearest Relevant Composition Specification
		BS: 2870	ISO	JIS
Leaded Brass	Cu -: 58% - 60%  Pb -: 1.5% - 2.5% Total Imp -: 0.3% (Max.) Zn -: Remaining	CZ 120	426/2 CuZn39 Pb2	H 3100 C 3713
* Material confirming to other National Specification e.g. ASTM, DIN etc. is also provided. * Available in Strips, Sheets, Plates & Circles form.

 

 

TYPICAL MECHANICAL PROPERTIES AS PER : B.S. : 2870
Material	Temper	Tensile Strength N/mm2	Elongation% on 50 mm G.L.	Vickers Hardness VPN	ISO	JIS
CZ 120	1/2H	-	10 Min	110 - 140	426/2	H 3100
	H	510 Min	5Min	140- 165	CuZn39Pb2	C3713
	HE	575 Min	3Min	165 - 190